Product performance and features:
- Active printing suitable for cotton, linen cellulose, and silk fabrics.
- Purely natural plant-based gum with a polysaccharide structure, offering excellent chemical stability and allowing for long-term storage without the addition of preservatives.
- Product boasts a high solids content of over 75%, low viscosity, and excellent thickening performance.
- The high-solids working paste maintains low viscosity, with a PVI value greater than 0.5. This enables higher printing speeds while ensuring print quality.
- The product is an inert chemical with excellent compatibility with other chemical additives.
- The print has high clarity and excellent color yield.
- Excellent degumming performance, with a hand feel superior to ordinary sizing agents.
General physical and chemical properties:
Chemical composition: Chemically modified herbal fibers + other natural plant gums. Ionic nature: Anionic, Non-ionic Supply Form White powdery substance 1% Viscosity (20°C) Approximately 100 mPa·s pH value (1% concentration) Approximately 6.5–7.5 Solubility: Stirring dissolves easily in water, quickly forming a paste. Application Technical Documentation:
I. Overview of XA-SIC® SC RP-06:
1. Suitable for reactive dye printing and pad-dyeing processes.
2. High solids content and low viscosity, easily soluble in water under stirring conditions—complete pulp preparation can be achieved after 40 minutes at a speed of 1800 r/min.
3. It exhibits excellent chemical compatibility and does not affect the viscosity of SC RP-06 when mixed with other additives.
4. The modified herbal fibers in this product naturally possess excellent moisture-absorbing properties, resulting in exceptionally vibrant colors under the same conditions.
5. Due to their low molecular weight, the products easily release from the paste, thereby giving printed fabrics an exceptional hand feel.
II. Usage and Dosage
1. The dosage of XA-SIC® SC RP-06 depends on factors such as the type, specifications, and basis weight of the fabric to be printed. The actual usage should be determined based on the specific conditions of the production facility.
2. You can also choose to use it in combination with the urea substitute XA-SIC®AM Sub-U10, helping to reduce the amount of urea used.
3. When used in combination with acrylic thickeners, it helps reduce pulp-making costs.
Recommended pigment paste composition ratio:
XA-SIC® SC RP-06 1.0%～1.5%
XA-SIC®AM Sub-U10 1% (optional, can be omitted)
Polyacrylic thickener, 2% to 4%
Sodium carbonate or baking soda: 3% to 4%
Urea 8% to 15%
Dye-resisting salt 0.5%～1%
Application scenarios:
- When using XA-SIC® SC RP-06 for pulp preparation, the stirring speed must not be too high, as prolonged high shear can damage the structural viscosity of the pulp.
- Add the required amount of water
- Add XA-SIC® SC RP-06 while stirring, and gently stir until fully swelled.
- Add baking soda/soda ash and anti-staining salt, and dissolve thoroughly.
- Urea or its alternative XA-SIC®AM Sub-U10.
- Stir until a uniform working paste is formed
Storage Stability
From the date of manufacture, it can be stored for 12 months under dry and shade conditions. Before use, check whether it has clumped together.
Safety Precautions
For operational precautions as well as ecological and toxicological information, please refer to the Material Safety Data Sheet for XA-SIC® SC RP-06.
Product Specifications:
For product specifications, please refer to the XA-SIC® SC RP-06 product's factory specifications and test reports.
Inquire Now
If you have any questions, please leave us a message, we are happy to serve you
Recommended Products
Contact Person: Hu Manager
Tel：15715853015
Email：964253538@qq.com
Address: No. 2 Pingjiang Road, Zhongguancun·Shaoxing Shumuwang Science Park, Didang Street, Yuecheng District, Shaoxing City, Zhejiang Province